CEMENT BASED, SINGLE COMPONENT WATERPROOFING MORTAR - CAPILLARY EFFECT
Product Description:
It is a capillary effective plaster and waterproofing material, which consists of specially selected cement and fillers and various effective chemicals, can be applied positively and negatively, and provides solutions in cases such as paint blisters and plaster spills.
It is suitable for TS EN 1504-2 (C) I MC-IR prenciples.
Public Works Pos No: 04.477/2
Areas of Use:
Indoor and outdoor,
Vertically and horizontally,
Especially in the insulation of basements from inside and outside,
Foundations, curtain and retaining walls,
On terraces (provided that it is protected)
Pre-ceramic waterproofing in wet areas such as WC, bathroom, kitchen and balcony,
It is used on surfaces such as concrete, plaster, alum.
Features:
It is easily prepared and applied.
It forms a waterproof layer before finishing materials such as tiles, ceramic, granite or screed.
It can be applied with a brush, trowel or spray machine.
Long working time.
It has high adhesion performance.
It creates a jointless, jointless, permanent, waterproof coating.
It is water vapor permeable.
It is resistant to freezing-thawing cycle.
It can be used safely in drinking water tanks.
Technical Spesifications:
Structure of the Material: Contains Mineral Filler, Special Cement and Chemicals.
Appearance: Gray Powder
Adhesion Strength: ≥ 1,00 N / mm²
Pressurized Water Resistance: ≥ 1.00 bar positive
Capillary Water Absorption: 0.1 g
Application Temperature: + 5ºC to + 25ºC
Service Temperature: -20 C to + 80 C
Rest Time of Mortar: 3-5 min.
Using Time: 1-2 hours
Time to Use: Mechanical Strength: 2 Days, Water Impermeability: 7 Days
Coating: 3 Days (Plaster, Ceramic etc.)
The above values are given for +23 ºC and 50% relative humidity.
Pre-Application Preparation:
Make sure that the application surface is cured and solid.
The surface to be applied should be free from paint, oil, dust etc. must be cleaned from materials.
Plasters that do not adhere well on the application surface should be removed, and any defects should be corrected with Tamires repair mortars. Active water leaks should be filled with suitable products.
The corners and edges should be chamfered with a radius of at least 4 cm. The application surface should be wetted thoroughly and wait until it becomes wet-dry.
If the coating material loses its water immediately and acquires a matt appearance during the application, it is understood that the surface is not wetted sufficiently or that it dries quickly.
In such cases, when the weather is hot or the material is in the wind, the mixing water of the material can be increased by 10% only for the first layer.
Water Mixing Ratio:
4,5-5,5 Liter / Bag
It changes according to the application type.
Application:
The appropriate amount of water is poured into a clean mixing bucket with the help of a scale.
Sumax Mono is added slowly for 3-5 minutes until a homogeneous and lump-free mixture is obtained. It is mixed and approximately 5 min. rested and again 30 sec. After mixing, the material becomes ready.
The homogeneous mortar is applied with a brush, roller or trowel.
Mix the prepared mortar for 30-60 minutes at the latest. Consume within.
The prepared mixture is applied in 2 or 3 layers with the help of a brush and roller. Brush application direction in each layer should be perpendicular to each other.
Wait approximately 2 hours between coats in 2 coats application with a brush or roller. Waiting time between coats may vary depending on ambient conditions.
In practice, wet film thickness should not exceed 2 mm in a single layer. The application should be made at least in 2 layers.
Round the corner joints in the application area and reinforce the mortar with a net.
In order to meet the tensile stresses on the moving floors with the risk of cracking and to create a more flexible waterproofing layer, a mesh can be placed between the application as a layer.
Working and reaction times of cement and polymer based systems are affected by the environment and ground temperature and relative humidity in the air. Reaction slows down at low temperatures, which increases pot life and working time. High temperatures accelerate the reaction and the times stated above decrease accordingly. For the material to complete its curing, the ambient and ground temperature should not fall below the allowed minimum temperature.
Sumax Mono applied at +23 ºC gains mechanical strength after 2 days, becomes waterproof after 7 days and reaches final strength after 14 days.
Later, you can cover it with coating material such as screed, ceramic, tile.
Warnings:
Avoid application at temperatures below + 5ºC and above + 25ºC.
Newly completed applications should be protected against adverse weather effects such as direct sunlight, excessive air flow, high air temperature (above + 35ºC), rain and frost in the first days.
Avoid direct contact with water within the first 24 hours of the completed application.
Never add powder and water to the expired or crusted mortar in the container, throw away the mortar.
Consumption:
1st floor Consumption: 1,4-1,6 kg / m² (for 1 mm thickness)
2nd Layer Consumption: 1,2-1,4 kg / m² (for 1 mm thickness)
3rd floor Consumption: 1.0-1.2 kg / m² (for 1 mm thickness)
The amount of consumption is the values calculated theoretically in the laboratory environment; We recommend that consumption control sample application be made before the application.
Packing: 20 kg craft bag.
Storage and Shelf Life:
It should be stored in its unopened original package, in a cool and dry environment, protected from frost. For short term storage, maximum 3 palettes should be placed on top of each other and the shipment should be made on a first in, first out system.
Palettes should not be stacked on top of each other during long term storage.
It is 12 months from the date of production under suitable storage conditions.
Opened packages should be stored under appropriate storage conditions and used within one week.
Safety Advices:
For more detailed information, please refer to the Safety Data Sheet.
Responsibility:
The application instructions and technical values given in this technical document are based entirely on our scientific and practical knowledge. These values may vary depending on the ambient conditions. Allmax Construction Chemicals reserves the right to make changes in products in line with technological developments. Allmax Yapı Kimyasalları cannot be held responsible for the results that may arise out of written recommendations regarding where and how the product will be used and / or due to incorrect use. Therefore, when using Allmax Construction Chemicals products, make sure that you use the right product in the right place. Allmax Construction Chemicals is only responsible for the quality of the product.